Michelle Vossen

Back to overview

Glove molding experiments

Molding with bioplastic

I used alginate bioplastic recipes for this, described here. The one I used for my first attempt is the flexible bioplastic, the other one the flexible biofoil recipe (the second try).

My first attempt failed miserably, because I used cling film to cover the mold. Of course the mixture cannot go between the fingers if there is plastic covering it so that was a bit stupid. Once the alginate started reacting with the calcium chloride sprayed on it, holes started forming because there was not enough of the mixture on the mold. At that point I just removed it from the mold because it didn’t look very promising.

mold mold result

To make sure I could cast directly on the mold without the risk of the plastic getting stuck on the foam, I coated it with exterior primer and lacquer (this one and this one). I then made a second attempt at casting without fabric on the mold, but the biggest issue is gravity. The mixture forms puddles between the fingers and doesn’t really want to keep the shape of the fingers, especially when sprayed.

mold mold

I cast two layers directly on the mold while spraying in between the two layers, but this doesn’t work well because the second layer will react with the first layer’s calcium chloride, so you just end up with two sheets that are loosely sticking together in a few places.

mold mold mold

At first I thought it would still keep the shape, but I removed it from the mold to let it dry which was a mistake, as it completely flattened.

end result

After that I pinned fabric to the mold and painted instead of cast it directly on the fabric.

mold mold result

Painting instead of casting got rid of some of the issues like puddle forming, but you do see the brush strokes and it looks a bit messy.

mold mold mold

mold mold

Drying the glove (on the right is after 24 hours):

mold mold

Once fully dried, this version has a bit more of a three dimensional shape compared to the previous two attempts, but it’s still pretty flat, and there is still too much residue between the fingers.

My conclusion is that alginate bioplastic is too flexible and shrinks too much for this to work.

Molding with textile hardener (Paverpol)

Since bioplastic didn’t work I had to try something else so my next attempt was with Paverpol. This actually worked pretty well (with varying levels of success) since it doesn’t shrink and you just need to paint it on top of the fabric, no other preparation needed.

Cotton twill:

mold mold

Polyester jersey works very well; coated fabric not so much since the fabric doesn’t absorb the textile hardener. It still kept a bit of the shape since the Paverpol dried as a layer on top of the coating.

mold

mold

For the tests below I used fabric that I laserengraved and lasercut. The laserengraved fabric was too stretchy and couldn’t keep the shape of the mold. The lasercut fabric was too fragile so when I tried taking it off the mold it ripped and parts of it got stuck to the mold.

Flour and water glue